Tra-Con Tra-Bond 2106T Fast Cure Thixotropic Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond 2106T Fast Cure Thixotropic Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND 2106T is an exceptional epoxy formulation recommended for lower temperature or wet industrial bonding applications where FAST CURING is required. This versatile two-part epoxy system contains no solvents, mixes easily at room temperature, and is suitable for high performance structural bonding applications where the combination of very fast room temperature curing coupled with low shrinkage and excellent mechanical and electrical properties is needed. It develops strong, tough bonds to metals, plastics, glass and glass fabrics, hardboards and forestry products, ceramics, rubber, masonry materials, and other construction materials. When fully cured, TRA-BOND 2106T is an excellent electrical insulator, and provides superior resistance to vapors and gases, water, galvanic action, petroleum fuels, salt solutions, and many other organic and inorganic compounds. TRA-BOND 2106T develops significant properties 1 hour after mixing. However, an extended cure of 4-6 hours at 25°C is required for fully matured bonds. Note: TRA-BOND 2106T develops a high exotherm. Use immediately after mixing. The exothermic reaction begins within 2 minutes after initiating the mixing step, so have everything ready before removing the BIPAX clamp.Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
Mixed
Solids Content 100 %
100 %
Reactive Solids Content
Viscosity 3600 cP
3600 cP
Mixed
Mechanical Properties Metric English Comments
Hardness, Shore D 25
25
After 10 min
67
67
After 30 min
72
72
After 60 min
Adhesive Bond Strength 1.38 MPa
200 psi
Lap shear, alum to alum
Izod Impact, Notched 1.01 J/cm
1.90 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 115 °C
239 °F
150 °C
302 °F
Intermittent
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
-60.0 °C
-76.0 °F
Intermittent
Glass Transition Temp, Tg 25.0 °C
77.0 °F
Ultimate Tg
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+11 ohm-cm
5.00e+11 ohm-cm
Dielectric Constant 4.8

@Frequency 1000 Hz
4.8

@Frequency 1000 Hz
Dielectric Strength 16.1 kV/mm
410 kV/in
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 65.0 °C
1.00 hour

@Temperature 149 °F
240 - 360 min

@Temperature 25.0 °C
4.00 - 6.00 hour

@Temperature 77.0 °F
Pot Life 5.0 min
5.0 min
Descriptive Properties Value Comments
Color Hazy, Light Straw
Mix Ratio, parts by weight 110/93
Resin/Hardener