Toyobo TS501 PPS, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler
Manufacturer Toyobo
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo TS501 PPS, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Feature: High stiffnessHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent physical, electrical, and thermal properties, corrosion resistant, and inherently flame retardant. PPS resins are used in the electrical, electronic, automotive, and industrial machinery industries.Information provided by Toyobo Co., Ltd
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ASTM D792
Water Absorption 0.020 %
0.020 %
24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D785
Tensile Strength, Ultimate 200 MPa
29000 psi
ASMT D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Modulus of Elasticity 18.7 GPa
2710 ksi
ASMT D638
Flexural Yield Strength 281 MPa
40800 psi
Flexural elongation is 2.1%; ASTM D790
Flexural Modulus 14.7 GPa
2130 ksi
ASMT D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 7.00 µm/m-°C

@Temperature 20.0 °C
3.89 µin/in-°F

@Temperature 68.0 °F
MD
CTE, linear, Transverse to Flow 61.0 µm/m-°C

@Temperature 20.0 °C
33.9 µin/in-°F

@Temperature 68.0 °F
Melting Point 282 °C
540 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
ASTM D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.8

@Frequency 1e+6 Hz
3.8

@Frequency 1e+6 Hz
ASTM D150
3.9

@Frequency 1000 Hz
3.9

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 12.0 kV/mm
305 kV/in
ASTM D149
Dissipation Factor 0.0014

@Frequency 1e+6 Hz
0.0014

@Frequency 1e+6 Hz
ASTM D150
0.0017

@Frequency 1000 Hz
0.0017

@Frequency 1000 Hz
ASTM D150
Arc Resistance 133 sec
133 sec
ASTM D495
Comparative Tracking Index 165 V
165 V
IEC test