Toyobo T-400 Nylon, 15% Glass-Reinforced
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-400 Nylon, 15% Glass-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: G.F. 15%Information provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 3.00 mm |
0.0070 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 3.00 mm |
0.011 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 113 MPa | 16400 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Modulus of Elasticity | 5.90 GPa | 856 ksi | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
| Compressive Yield Strength | 108 MPa | 15700 psi | ASTM D695 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17 wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C @Temperature 20.0 °C |
19.4 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | unregistered |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.010 | 0.010 | ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Comparative Tracking Index | 550 V | 550 V | IEC test |
Users viewing this material also viewed the following:
- Nye Lubricants 132H (SO) Synthetic Oil
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 350ºF Cure Temperature
- Indium Corp. 6N5 High Purity Indium Metal
- Lubrizol Advanced Materials Pearlbond® 180 Thermoplastic Polyurethane
- Plenco 4504 Phenolic, Granular, Compression Molded
- Azoty Tarnow™ Tarnamid® T-29 Polyamide 6 - Natural
- Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Longitudinal Properties
- 3M 2125 Polyethylene Protective Tapes
Copyright © lookpolymers.com All Rights Reserved