Toyobo PELPRENE™ S9001 Polyester TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ S9001 Polyester TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPEInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.28 % | 0.28 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 10 g/10 min @Temperature 230 °C |
10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 99 | 99 | JIS K6301 |
| Hardness, Shore D | 78 | 78 | ASTM D2240 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| 50% Modulus | 0.0441 GPa | 6.40 ksi | ASTM D638 |
| Flexural Modulus | 0.882 GPa | 128 ksi | ASTM D790 |
| Compressive Modulus | 0.0392 GPa | 5.69 ksi | 0.1; ASTM D695 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Tear Strength | 250 kN/m | 1430 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 6.0 | 6.0 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 223 °C | 433 °F | By DSC |
| Maximum Service Temperature, Air | 146 °C | 295 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 207 °C | 405 °F | ASTM D1525 |
| Brittleness Temperature | -50.0 °C | -58.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+15 ohm-cm | 7.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature
- DuPont Performance Polymers Zytel® 73G30HSL NC010 Nylon 6 (Unverified Data**)
- Haynes Hastelloy® alloy X 12.7 mm plate weldments
- Wanhua Chemical Wanthane® WHT-1295 Polyester Based TPU
- DuPont Performance Polymers Kalrez® 6375UP FFKM Perfluoroelastomer
- Bapolene® 122F Polyethylene, Film Grade
- AdvanSource Biomaterials ChronoFlex® C 75D Biodurable Medical Grade Polyurethane
- Arkema Group Evatane® 1020 VB 2 Ethylene Vinyl Acetate
- Fainplast Compounds MPH 75/D Medical Flexible PVC, Extrusion
- Fainplast Compounds PK 77/K-FR Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved