Toyobo PELPRENE™ S2004FS Polyester TPE, Flame Resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ S2004FS Polyester TPE, Flame Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Flame ResistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.38 % | 0.38 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 12 g/10 min @Temperature 230 °C |
12 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 98 | 98 | JIS K6301 |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Tensile Strength at Break | 27.2 MPa | 3950 psi | ASTM D638 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| 50% Modulus | 0.0201 GPa | 2.92 ksi | ASTM D638 |
| Flexural Modulus | 0.290 GPa | 42.1 ksi | ASTM D790 |
| Compressive Modulus | 0.0192 GPa | 2.78 ksi | 0.1; ASTM D695 |
| Resilience | 60 | 60 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 155 kN/m | 884 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 12 | 12 | ASTM D1044 |
| Compression Set | 65 % | 65 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 210 °C | 410 °F | By DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 185 °C | 365 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE144H PC
- Reliance Industries PET - 35% Glass filled
- Shell Carilon® DB6G3A10 Polyketone, 15% Glass-Reinforced General-Purpose Injection Molding Grade (discontinue
- SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS
- Master Bond EP21TDCS Silver Filled Electrically Conductive Epoxy Compound
- Master Bond MasterSil 710 Silicone Paste Meets MIL Spec
- Unifrax Excelfrax® 1800 Flexliner Microporous Insulation
- Chase Plastics CP Pryme® NN100STL (DAM) Nylon 66, Super Toughened, Internally Lubricated
- A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-990 (MT)
Copyright © lookpolymers.com All Rights Reserved