Toyobo GLAMIDE® T-669VGB Nylon-66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-669VGB Nylon-66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-669VGB is a flame resistant Nylon-66. It is of halogen origin and contains 35% GF.35
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 35 % | 35 % | |
| Water Absorption | 0.60 % | 0.60 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0050 - 0.0080 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0080 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 25 g/10 min | 25 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Practical Use; ASTM-D638 |
| 125 MPa @Temperature 80.0 °C |
18100 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 145 MPa @Temperature 23.0 °C |
21000 psi @Temperature 73.4 °F |
Practical Use; ASTM-D638 | |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 210 MPa @Temperature -40.0 °C |
30500 psi @Temperature -40.0 °F |
Practical Use; ASTM-D638 | |
| 230 MPa @Temperature -40.0 °C |
33400 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Absolute Drying; ASTM-D638 |
| 3.0 % | 3.0 % | Practical Use; ASTM-D638 | |
| Flexural Strength | 130 MPa @Temperature 80.0 °C |
18900 psi @Temperature 176 °F |
Practical Use; ASTM-D790 |
| 160 MPa @Temperature 80.0 °C |
23200 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 190 MPa @Temperature 23.0 °C |
27600 psi @Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 240 MPa @Temperature 23.0 °C |
34800 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 270 MPa @Temperature -40.0 °C |
39200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 5.40 GPa @Temperature 80.0 °C |
783 ksi @Temperature 176 °F |
Practical Use; ASTM-D790 |
| 7.00 GPa @Temperature 80.0 °C |
1020 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 8.00 GPa @Temperature 23.0 °C |
1160 ksi @Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 11.3 GPa @Temperature 23.0 °C |
1640 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 13.0 GPa @Temperature -40.0 °C |
1890 ksi @Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 14.0 GPa @Temperature -40.0 °C |
2030 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 1.05 J/cm @Temperature -40.0 °C |
1.97 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.10 J/cm @Temperature -40.0 °C |
2.06 ft-lb/in @Temperature -40.0 °F |
Practical Use; ASTM-D256 | |
| 1.40 J/cm @Temperature 23.0 °C |
2.62 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
Practical Use; ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 26 | 26 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | Practical Use; ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Dielectric Strength | 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
Practical Use; ASTM-D149 |
| 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Arc Resistance | 110 sec | 110 sec | Absolute Drying; ASTM-D495 |
| Comparative Tracking Index | 300 V | 300 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Injection Pressure | 40.0 MPa | 5800 psi |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T20040 Polypropylene Copolymer, Mineral Reinforced
- ExxonMobil Escor® AT-320 EMAAA Terpolymer for Polymer Modification (discontinued **)
- Techmer ES HiFill® PA6/6 GF10 TL10 BK 10% Glass Filled
- Saint-Gobain CHR® SGB6-10(R) CHEMLAM Brown Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- SK Chemicals SKYTHANE® 180A R series Polyurethane
- Hexcel® HexPly® F155 Epoxy Resin, 220 Glass Fabric
- Chosun Refractories SAL99 Special High Alumina brick
- Anderman Ceramics EREH99 Hafnium Oxide, High Purity
Copyright © lookpolymers.com All Rights Reserved