Toyobo GLAMIDE® T-663G15 Nylon-66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer	Toyobo
Trade Name	GLAMIDE®
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Toyobo GLAMIDE® T-663G15 Nylon-66.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-663G15 is a GF reinforced Nylon-66. It contains 15% GF.15

Physical Properties	Metric	English	Comments
Specific Gravity	1.26 g/cc	1.26 g/cc	Absolute Drying; ASTM-D792
Filler Content	15 %	15 %
Water Absorption	1.0 %	1.0 %	Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium	2.1 %	2.1 %	Absolute Drying; ASTM-D570
Linear Mold Shrinkage	0.0070 - 0.010 cm/cm <br>@Thickness 1.00 mm	0.0070 - 0.010 in/in <br>@Thickness 0.0394 in	Absolute Drying
	0.0080 - 0.011 cm/cm <br>@Thickness 3.00 mm	0.0080 - 0.011 in/in <br>@Thickness 0.118 in	Absolute Drying
Melt Flow	10 g/10 min	10 g/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	Absolute Drying; ASTM-D785
Tensile Strength, Ultimate	45.0 MPa <br>@Temperature 80.0 °C	6530 psi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.1%); ASTM-D638
	60.0 MPa <br>@Temperature 80.0 °C	8700 psi <br>@Temperature 176 °F	Absolute Drying; ASTM-D638
	90.0 MPa <br>@Temperature 23.0 °C	13100 psi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.1%); ASTM-D638
	120 MPa <br>@Temperature 23.0 °C	17400 psi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D638
	145 MPa <br>@Temperature -40.0 °C	21000 psi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D638
	160 MPa <br>@Temperature -40.0 °C	23200 psi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D638
Elongation at Break	3.5 %	3.5 %	Absolute Drying; ASTM-D638
	7.0 %	7.0 %	Practical Use (Water Absorption 2.1%); ASTM-D638
Flexural Strength	75.0 MPa <br>@Temperature 80.0 °C	10900 psi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	100 MPa <br>@Temperature 80.0 °C	14500 psi <br>@Temperature 176 °F	Absolute Drying; ASTM-D790
	120 MPa <br>@Temperature 23.0 °C	17400 psi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	160 MPa <br>@Temperature 23.0 °C	23200 psi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D790
	170 MPa <br>@Temperature -40.0 °C	24700 psi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	200 MPa <br>@Temperature -40.0 °C	29000 psi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D790
Flexural Modulus	2.10 GPa <br>@Temperature 80.0 °C	305 ksi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	2.50 GPa <br>@Temperature 80.0 °C	363 ksi <br>@Temperature 176 °F	Absolute Drying; ASTM-D790
	3.50 GPa <br>@Temperature 23.0 °C	508 ksi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	5.40 GPa <br>@Temperature 23.0 °C	783 ksi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D790
	5.90 GPa <br>@Temperature -40.0 °C	856 ksi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
	6.20 GPa <br>@Temperature -40.0 °C	899 ksi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D790
Izod Impact, Notched	0.500 J/cm <br>@Temperature -40.0 °C	0.937 ft-lb/in <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D256
	0.550 J/cm <br>@Temperature -40.0 °C	1.03 ft-lb/in <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.1%); ASTM-D256
	0.700 J/cm <br>@Temperature 23.0 °C	1.31 ft-lb/in <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D256
	1.10 J/cm <br>@Temperature 23.0 °C	2.06 ft-lb/in <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.1%); ASTM-D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	262 °C	504 °F	Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	Absolute Drying; ASTM-D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+9 - 1.00e+10 ohm-cm	1.00e+9 - 1.00e+10 ohm-cm	Practical Use (Water Absorption 2.1%); ASTM-D257
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	Absolute Drying; ASTM-D257
Dielectric Constant	4.0 <br>@Frequency 1000 Hz	4.0 <br>@Frequency 1000 Hz	Absolute Drying; ASTM-D150
Dielectric Strength	18.0 kV/mm <br>@Thickness 2.00 mm	457 kV/in <br>@Thickness 0.0787 in	Practical Use (Water Absorption 2.1%); ASTM-D149
	24.0 kV/mm <br>@Thickness 2.00 mm	610 kV/in <br>@Thickness 0.0787 in	Absolute Drying; ASTM-D149
Dissipation Factor	0.010 <br>@Frequency 1000 Hz	0.010 <br>@Frequency 1000 Hz	Absolute Drying; ASTM-D150
Arc Resistance	90 sec	90 sec	Practical Use (Water Absorption 2.1%); ASTM-D495
	110 sec	110 sec	Absolute Drying; ASTM-D495
Comparative Tracking Index	575 V	575 V	IEC Method

Processing Properties	Metric	English
Melt Temperature	280 - 310 °C	536 - 590 °F
Mold Temperature	60.0 °C	140 °F
Injection Pressure	30.0 - 60.0 MPa	4350 - 8700 psi