Toyobo GLAMIDE® T-602G30 MXD66
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-602G30 MXD66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-602G30 is a GF reinforced, aromatic MXD66 nylon. It has a good appearance and contains 30% GF.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.80 % | 0.80 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0040 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 22 g/10 min | 22 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 72.0 MPa @Temperature 80.0 °C |
10400 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 |
| 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 115 MPa @Temperature 23.0 °C |
16700 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 | |
| 190 MPa @Temperature 23.0 °C |
27600 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 235 MPa @Temperature -40.0 °C |
34100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 | |
| 260 MPa @Temperature -40.0 °C |
37700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.6 % | 3.6 % | Absolute Drying; ASTM-D638 |
| 4.2 % | 4.2 % | Practical Use (Water Absorption 1.7%); ASTM-D638 | |
| Flexural Strength | 95.0 MPa @Temperature 80.0 °C |
13800 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 |
| 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 140 MPa @Temperature 80.0 °C |
20300 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 260 MPa @Temperature -40.0 °C |
37700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 3.20 GPa @Temperature 80.0 °C |
464 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 |
| 4.00 GPa @Temperature 23.0 °C |
580 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 4.00 GPa @Temperature 80.0 °C |
580 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 8.50 GPa @Temperature 23.0 °C |
1230 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 9.20 GPa @Temperature -40.0 °C |
1330 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 10.0 GPa @Temperature -40.0 °C |
1450 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.650 J/cm @Temperature -40.0 °C |
1.22 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.800 J/cm @Temperature -40.0 °C |
1.50 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D256 | |
| 1.25 J/cm @Temperature 23.0 °C |
2.34 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 2.10 J/cm @Temperature 23.0 °C |
3.93 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | Practical Use (Water Absorption 1.7%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.7%); ASTM-D149 |
| 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 90 sec | 90 sec | Practical Use (Water Absorption 1.7%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 2710 TRN 9470 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Plastcom PLASTAMID® 6 BT N 32 B/IM PA6
- Kotec Carbotex K-50UV Polycarbonate, General Purpose, UV Stability Grade
- Schott N-PSK3 Glass
- Schott S8802 Contrast Enhancement Filter
- Techmer ES HiFill® PA6/6 GF30 HS L BK 30% Glass Filled
- SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66
- Tra-Con Tra-Bond 933-2 Moisture Resistant Chip Encapsulant
- Denka VINYKON S210050 PVC, S grade for transparent extrusion molding
Copyright © lookpolymers.com All Rights Reserved