Total PSC 1810/1811 Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer	Total Atofina
Trade Name	PSC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PSC 1810/1811 Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

1811 is a very easy flowing crystal polystyrene designed, principally, for the injection molding industry. The excellent processing characteristics of this grade allows for the production of articles which are very thin and/or have complex flow patterns. In extrusion, 1810 is used as a high capping layer in co-extrusion. 1810 is not externally lubricated.ApplicationInformation provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines. This product was previously known as LACQRENE®

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	ISO 62
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Melt Flow	20 g/10 min @Load 5.00 kg, Temperature 200 °C	20 g/10 min @Load 11.0 lb, Temperature 392 °F

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	70	70	ISO 2039-2
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527-2
Elongation at Break	2.0 %	2.0 %	ISO 527-2
Tensile Modulus	3.10 GPa	450 ksi	ISO 527-2
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Charpy Impact Unnotched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear	71.0 µm/m-°C @Temperature 20.0 °C	39.4 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	81.0 °C	178 °F	Annealed; ISO 75-2A
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F	Unannealed; ISO 75-2A
Vicat Softening Point	85.0 °C	185 °F	50N (T° increase = 5°C/h); ISO 306B50
	90.0 °C	194 °F	10N (T° increase = 50°C/h); ISO 306A50

Electrical Properties	Metric	English	Comments
Surface Resistivity per Square	>= 1.00e+14 ohm	>= 1.00e+14 ohm	ISO IEC93
Dielectric Strength	135 kV/mm	3430 kV/in