UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 57 | 57 | ASTM D412 |
| Tensile Strength at Break | 14.6 MPa | 2120 psi | ASTM D412 |
| Elongation at Break | 470 % | 470 % | ASTM D412 |
| 100% Modulus | 0.00190 GPa | 0.276 ksi | ASTM D412 |
| 200% Modulus | 0.00450 GPa | 0.653 ksi | ASTM D412 |
| 300% Modulus | 0.00800 GPa | 1.16 ksi | ASTM D412 |
| Rebound | 51 % | 51 % | BS.903,PART22 |
| Tear Strength | 39.0 kN/m | 223 pli | ASTM D624 |
| Abrasion | 71 | 71 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 154 | 154 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 20 % | 20 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 3300 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 18% | ASTM D623 (40°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 19 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Mitsui ADMER® NF908A PE Type Polyolefin
- Lehmann & Voss LUVOCOM® 1105-1963 PEEK, with glass fiber
- Lucite International Elvacite ® 3001 Acrylic Resin
- Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Dry
- Techmer ES Luriblend® PC CF15 TL6 BK 15% Carbon Filled
- Techmer ES HiFill® TPX-HTN-01092 A 50% Glass Filled
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- Trelleborg AEM Eccospheres® IGD-101 Sodium Borosilicate Glass Microspheres
- Compuestos Dominicanos Polycom AU-050595 PVC Compound
- Aptek 7504LM-PMF UV Urethane Coating/Encapsulant
Copyright © lookpolymers.com All Rights Reserved