Total PPC 4660 Polypropylene, Heterophasic Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Total Atofina
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPC 4660 Polypropylene, Heterophasic Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATOFINA Polypropylene PPC 4660 is heterophasic copolymer.
Physical Properties Metric English Comments
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 3.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 82
82
ISO 2039-2
Tensile Strength, Yield 25.0 MPa
3630 psi
ISO 527-2
Elongation at Yield 7.0 %
7.0 %
ISO 527-2
Tensile Modulus 1.10 GPa
160 ksi
ISO 527-2
Flexural Modulus 1.20 GPa
174 ksi
ISO 527-2
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 179
5.50 kJ/m²

@Temperature -20.0 °C
 2.62 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179
0.700 J/cm²

@Temperature -20.0 °C
 3.33 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
120°C per hour; ISO 75-2
Vicat Softening Point 65.0 °C
149 °F
50N-50°C per hour; ISO 306
135 °C
275 °F
10N-50°C per hour; ISO 306