ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LL 6235 is a narrow molecular weight butene copolymer designed for applications that require easy processability in thin walled parts. This resin offers outstanding toughness and tear resistance in freezer applications for food packaging.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	ASTM D4883
Environmental Stress Crack Resistance	<= 1.0 hour	<= 1.0 hour	Condition B, 10%; ASTM D1693
Melt Flow	35 g/10 min @Load 2.16 kg, Temperature 190 °C	35 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.00 MPa	1595 psi	ASTM D638
Elongation at Break	116 %	116 %	ASTM D638
Flexural Modulus	0.250 GPa	36.2 ksi	1% secant; ASTM D790
Tensile Impact Strength	233 kJ/m² @Temperature -40.0 °C	111 ft-lb/in² @Temperature -40.0 °F	ASTM D1822

Thermal Properties	Metric	English	Comments
Melting Point	124 °C	255 °F	ASTM D3418
Crystallization Temperature	106 °C	223 °F	ASTM D3418
Vicat Softening Point	92.2 °C	198 °F	ASTM D1525
Brittleness Temperature	>= -70.0 °C	>= -94.0 °F	ASTM D746

Descriptive Properties	Value	Comments
Features	Standard processing antioxidants
Form	PELLET