Total Lumicene® mPE M5510 EP Metallocene Polyethylene, Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Total Atofina
Trade Name Lumicene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lumicene® mPE M5510 EP Metallocene Polyethylene, Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product is a Total Ecosolutions grade.Lumicene® mPE M5510 EP is a second generation metallocene high density homopolymer polyethylene.Lumicene® mPE M5510 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The outstanding stiffness combined with good optical properties brings a significant downgauging potential.The high density of Lumicene® mPE M5510 EP enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE.Lumicene® mPE M5510 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, heavy-duty sacks, automatic packaging specialty film, mailing film and lamination.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.955 g/cc
0.955 g/cc
ISO 1183
Thickness 40.0 microns
1.57 mil
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 27.5 MPa
3990 psi
ISO 527-3
Film Tensile Strength at Yield, TD 28.0 MPa
4060 psi
ISO 527-3
Film Elongation at Break, MD 870 %
870 %
ISO 527-3
Film Elongation at Break, TD 910 %
910 %
ISO 527-3
Elmendorf Tear Strength, MD 1.10 g/micron
27.9 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 9.20 g/micron
234 g/mil
ISO 6383-2
Dart Drop Test 100 g
0.221 lb
ISO 7765-1
Film Tensile Strength at Break, MD 57.0 MPa
8270 psi
ISO 527-3
Film Tensile Strength at Break, TD 45.0 MPa
6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 134 °C
273 °F
ISO 11357
Vicat Softening Point 133 °C
271 °F
ISO 306
Optical Properties Metric English Comments
Haze 24 %
24 %
ISO 14782
Gloss 40 %
40 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 200 - 230 °C
392 - 446 °F
Blow Molding
Melt Temperature 210 °C
410 °F
Extrusion
Die Opening 0.0800 - 0.280 cm
0.0315 - 0.110 in
Blow-up Ratio (BUR) 1.5 - 4.5
1.5 - 4.5