Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | at 25°C |
| Mooney Viscosity | 48 @Temperature 121 °C |
48 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Peak value, at 25°C |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | |
| Tensile Strength, Yield | 2.80 MPa @Strain 100 % |
406 psi @Strain 100 % |
|
| Elongation at Break | 320 % | 320 % | |
| Tear Strength | 19.6 kN/m | 112 pli | at 25°C |
| Compression Set | 13 % | 13 % | 70 hours at 25°C |
| 12 % @Temperature 100 °C |
12 % @Temperature 212 °F |
70 hours | |
| 18 % @Temperature 175 °C |
18 % @Temperature 347 °F |
70 hours | |
| 32 % @Temperature 200 °C |
32 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -8.00 °C | 17.6 °F | TR test, TR10 |
| -5.00 °C | 23.0 °F | Gehman torsion test, T10 | |
| -2.00 °C | 28.4 °F | TR test, TR70 | |
| -1.30 °C | 29.7 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -26.0 °C | -14.8 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47N ABS
- Nitriflex Nitrimpact 1300 MBS Modifier
- Loxim 220 12V0 Polybutylene Terephthalate
- Zylog Hipolyene® 8021 M Thermoplastic Polyolefin & PP Compound
- Fainplast Compounds CL 64 Flexible PVC, Sheathing
- Braskem INSPIRE™ 114 Performance Polypropylene Polymer
- Asahi Glass Fluon® PA7115 15% Polyimide, PTFE Filled Compound
- Aclo Accutech Polypropylene CP0409HUUVV Copolymer UV Stabilized
- Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact
- DuPont Performance Polymers Delrin® 900P BK602 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved