- Teknor Apex Chemlon® 113 GH Nylon 66, 13% Short Glass Fiber Reinforced
Teknor Apex Chemlon® 113 GH Nylon 66, 13% Short Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 113 GH Nylon 66, 13% Short Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good creep Resistance; Good stiffness; Good dimensional stability; High strength; Heat stabilized Processing Method: Injection Molding Forms: Pellets Automotive Specifications: Chrysler MS-DB41 CPN2239 Color: BK001 Black; Chrysler MS-DB41 CPN3794 Color: Non-matched Color; Chrysler MS-DB41 CPN4061 Color: 100% Color Match; Ford ESA-M4D349-A; GM GMP.PA66.020Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 169 MPa | 24500 psi | ASTM D790 |
| Flexural Modulus | 4.65 GPa | 675 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Temperature 22.8 °C |
1.20 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm @Thickness 3.00 mm |
460 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 257 - 271 °C | 495 - 520 °F | |
| Front Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Nozzle Temperature | 263 - 282 °C | 505 - 540 °F | |
| Melt Temperature | 257 °C | 495 °F | |
| 263 - 282 °C | 505 - 540 °F | Processing Temperature | |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black; Natural Color | |
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- RheTech Products FT4900-33UV Thermoplastic Polyolefin, UV Stabilized, KSD Charcoal Argent
- Pasargad Polymer Peyvand Pasalen 3P-H3230B Polypropylene, 30% Mineral Filled Reinforced
- 3M Dyneon™ TF 5032R PTFE (discontinued **)
- Fainplast Compounds RE 330 Rigid PVC, Extrusion
- SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Europe-Africa-Middle East)
- Hexcel® HexWeb® HRH-36/OX - 3/16 - 2.0 Para-Aramid/Phenolic Core
- Clariant Renol 612G10-L Nylon 612, 10% Glass Fiber Reinforced, Lubricated
- Aclo Accutech Polypropylene Copolymer CP0437W30L Wollastonite Reinforced
- Beijing Chemical Industry KAIFA® HN301-G0 PA6 Resin
Copyright © lookpolymers.com All Rights Reserved