Teijin Multilon TN-7500 Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon TN-7500 Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has excellently high flowability, i.e., suitable for a large-scale business machine chassis.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527 |
| Elongation at Break | 50 % | 50 % | 50mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
Users viewing this material also viewed the following:
- Arlon 48571R005 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate (discontinued **)&l
- PolyOne Elastamax™ XL 1088-10 Styrene Butadiene Block Copolymer (SBC) with Mineral Filler (discontinued **)&l
- Materion Beryllium Copper Alloy 10C Castings (UNS C82000)
- Minelco FireCarb TEG-370 Expandable Graphite
- Solvay Specialty Polymers Ixan® SGA-1 Polyvinylidene Chloride (PVDC)
- Dow Corning SYL-OFF® 4000 CATALYST
- Braskem RP 347 Injection Molding Polypropylene
- Teknor Apex APEX® 84132 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved