Techmer ES Plaslube® NY-1/MS/5 NAT PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled |
| Manufacturer | Techmer ES |
| Trade Name | Plaslube® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plaslube® NY-1/MS/5 NAT PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | 24 Hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.34 GPa | 485 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Abatron 105A/50-12B Filled Potting Compound (discontinued **)
- Termopol Termoton® K2GA3060A TPE Compound, based on SEBS and Polyolefins
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate
- A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy
- Zylog Neoplast® 163 FT EB Thermoplastic Vulcanizate
- Lubrizol ESTANE® GP85AE Ester Based Thermoplastic Polyurethane
- A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66
- Dow Corning JCR 6101 UP
- Clariant 6004G13-HSL BK UV Black Nylon 6, 13% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved