Polykemi AB POLYabs XX0 ABS, Extrusion Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer Polykemi AB
Trade Name POLYabs
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYabs XX0 ABS, Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Melt Index of Compound 3.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
 3.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 42.0 MPa
<= 6090 psi
ISO/R527
Elongation at Yield 5.5 %
5.5 %
ISO/R527
Flexural Strength <= 66.0 MPa
<= 9570 psi
ISO 178
Flexural Modulus 1.85 GPa

@Temperature 23.0 °C
 268 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 1.70 J/cm²

@Temperature -20.0 °C
 8.09 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C
192 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
120°C/h; ISO 75/1
Vicat Softening Point 100 °C

@Load 5.001 kg
 212 °F

@Load 11.03 lb
 50°C/h; ISO 306
106 °C

@Load 1.00 kg
 223 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in