Techmer ES Luriblend® PA6/6 TS18 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 TS18 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE + Silicone Lubricant (18%)Features: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % @Time 86400 sec |
0.80 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.17 mm |
0.018 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Yield Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C | 45.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 215 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 85FS PC/ABS-Blend
- Pau Tai UNISTAB EC-2515 Solid Complex Stabilizer
- SABIC Innovative Plastics Lexan® ML6031 PC Copolymer (Asia Pacific)
- NanoAmor 90%, OD: 1-2 nm COOH Functionalized Single Walled Carbon Nanotubes
- Henkel Hysol EA 9628H Film Adhesive
- SABIC Innovative Plastics NORYL FP6130 PPE+PS (Asia Pacific)
- DSM Akulon® K225-KS Nylon 6 (European and Asian Grade) (Cond)
- ExxonMobil Santoprene® 8211-85M350 Thermoplastic Vulcanizate
- UBE UBESTA® 3030U Nylon 12 (After Sodium Hydroide for 1000 hours)
- Saint-Gobain Furon®, Kapton® K275 Tape
Copyright © lookpolymers.com All Rights Reserved