Techmer ES Luriblend® PA6/6 GF10 M/TL10 10% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 GF10 M/TL10 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: Molybdenum Disulfide Lubricant and PTFE LubricantFeatures: LubricatedAppearance: Natural ColorInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Water Absorption | 0.75 % @Time 86400 sec |
0.75 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 77.2 MPa | 11200 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 3.52 GPa | 510 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | ASTM D1894 |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D1894 |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.333 MPa-m/sec | 9500 psi-ft/min | 10 fpm |
| 0.333 MPa-m/sec | 9500 psi-ft/min | 1000 fpm | |
| 0.350 MPa-m/sec | 10000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C | 30.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 281-73MED Thermoplastic Elastomer (discontinued **)
- Polimeri Europa Europrene® N OZO 7033/60 NBR-PVC blend
- 3M Dyneon™ TF 5039 PTFE Dispersion (discontinued **)
- Honeywell Capran® Oxyshield™ M-OPA (0.75 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film
- Huntsman IROGRAN® PS 443-201 TPU-Polyester
- LG Chemical LUCON SE-4200H Electrically Conductive Thermoplastic
- Heraeus Cleviosâ„¢ P VP AI 4083 Conductive Sulfonate Polymer for Antistatic Coatings
- SABIC Innovative Plastics LNP STAT-KON DEI13F PC (Asia Pacific)
- Unitika TERRAMAC TE-8210 Polylactic Acid (PLA)
- Armstrong A-12 Epoxy Adhesive, at 2:3 Mix Ratio
Copyright © lookpolymers.com All Rights Reserved