Techmer ES Luriblend® PA6 CF30 TL15 BK 30% Carbon Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber/PTFE Reinforced |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6 CF30 TL15 BK 30% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant (15%)Features: Low Friction, Good Wear Resistance and LubricatedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.88 % @Time 86400 sec |
0.88 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 159 MPa | 23000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 252 MPa | 36500 psi | ASTM D790 |
| Flexural Modulus | 11.6 GPa | 1680 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D1894 |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D1894 |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.771 MPa-m/sec | 22000 psi-ft/min | 1000 fpm |
| 1.05 MPa-m/sec | 30000 psi-ft/min | 10 fpm | |
| 1.54 MPa-m/sec | 44000 psi-ft/min | 100 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1.00e+14 ohm-cm | <= 1.00e+14 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- GEHR Plastics Ultem 2300 PEI-30 GF 30% Glass Fiber Reinforced (discontinued **)
- Sylvin Technologies 9999-65 Natural PVC Molding Compound
- Teknor Apex APEX® 82-E254X-NL Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP Thermocomp RF008U PA 66 (Europe-Africa-Middle East)
- Loctite® 392 Rapid Fixture Structural Adhesive
- Covestro Bayblend® FR 3030 Polycarbonate + ABS, Flame Retardant Grade
- ExxonMobil HDPE HD 6706.17 High Density Polyethylene Copolymer Resin
- EPICHEM Epilac T ABS Acrylonitrile Butadiene Styrene
- Asahi Kasei Tenac® 5050 Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved