Techmer ES Luriblend® ABS X MB
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® ABS X MB.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Silicone LubricantFeatures: General Purpose and LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 64.8 MPa | 9400 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.01 J/cm @Thickness 3.17 mm, Temperature 0.000 °C |
1.90 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
ASTM D256 | |
| 2.78 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
5.20 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- LATI LARPEEK 50 G/60 60% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
- DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Lubriplate Special Auto Marine Grease Automotive Lubricant
- Lubrizol ESTANE® X1014 Ether Based Thermoplastic Polyurethane (European Grade)
- A. Schulman POLYBATCH™ White LL8350 AP Concentrate Based In LLDPE
- A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound
- ExxonMobil Label-Lyte® 150 LL-302 White Opaque OPP Facestock
- Aclo Accutech Polypropylene Homopolymer HP0336C30L Calcium Reinforced
- Resinlab® UR1049 MDI Based Rigid Polyurethane Foam System
Copyright © lookpolymers.com All Rights Reserved