Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Techmer ES Luriblend® ABS TL2

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), PTFE Filled
Manufacturer Techmer ES
Trade Name Luriblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Techmer ES Luriblend® ABS TL2.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0060 cm/cm

@Thickness 3.17 mm
 0.0060 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 4.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 4.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 103
103
ASTM D785
Tensile Strength, Yield 30.3 MPa
4400 psi
ASTM D638
Elongation at Break 3.5 %
3.5 %
ASTM D638
Flexural Strength 62.7 MPa
9100 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm,
Temperature -40.0 °C
 1.00 ft-lb/in

@Thickness 0.125 in,
Temperature -40.0 °F
 ASTM D256
1.01 J/cm

@Thickness 3.17 mm,
Temperature 0.000 °C
 1.90 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
 ASTM D256
2.67 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
 5.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 °C
219 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 77.8 °C
172 °F
Unannealed; ASTM D648
Users viewing this material also viewed the following: