Techmer ES HiFill® PP GB60 60% Glass Beads Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 60% Glass Fiber Filler |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GB60 60% Glass Beads Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 60% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % @Time 86400 sec |
0.040 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Yield Strength | 28.3 MPa | 4100 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C
- Sylvin Technologies 8940-70 Natural PVC Extrusion Compound
- Techmer ES Electrablend® PA12 CF13 L 13% Carbon Filled
- Teknor Apex ELEXAR® EL 8623 Thermoplastic Elastomer
- Polyram RamOfin PPH302G4 Polypropylene, 20% Glass Fiber
- Covestro Makrolon® SF805 Polycarbonate, 5% Glass Filled
- Hippe PF CP 204 Cellulose Paper Reinforced Phenolic Resin - Sheet
- DuPont Teijin Films Mylar® HP Polyester Film, 60 Gauge
- Arlon R32521R010 0.0095" (0.241 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Styrolution Luran® SAN C Styrene Acrylonitrile
Copyright © lookpolymers.com All Rights Reserved