Techmer ES HiFill® PP GB50 50% Glass Beads Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GB50 50% Glass Beads Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 50% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm |
0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Yield Strength | 29.6 MPa | 4300 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.2 µm/m-°C | 34.0 µin/in-°F | ASTM D696 |
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 N PP, basic type
- Mitsubishi Iupilon® E2000UR 5 MFI, UV Stabilized Polycarbonate With Release
- Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, Conditioned
- SABIC Innovative Plastics NORYL EXNL0357 PPE+PS
- American Elements Carbon Nanoparticles
- ChevronTexaco Inhibited Transformer Oil
- Axiall ProTherm® 4529 CPVC Rigid PVC, Molding
- Carmel Olefins CAPILENE® HU 75 AV Polypropylene Impact Copolymer
- Potters Industries A-Series P-0170 Soda-Lime Silica Technical Quality Solid Glass Spheres
- SABIC Innovative Plastics Lexan® 945 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved