Techmer ES HiFill® PA6 GF35 HS L 35% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6 GF35 HS L 35% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: Lubricated and Heat StabilizedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 195 MPa | 28300 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.82 J/cm @Thickness 3.17 mm |
3.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 13.3 J/cm @Thickness 3.17 mm |
25.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C | 17.0 µin/in-°F | ASTM D696 |
| Melting Point | 218 °C | 424 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® INP563 ABS
- Overview of materials for Styrene-Butadiene Copolymer, SBC
- HP Alloys Alloy 718, 10% Cold Worked
- DSM Stanyl® TW241F6 Nylon 46-30% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Cond)
- Eurotec® Tecodur® PB70 GR30 NL XA 20 PBT 30% glass fiber reinforced, UL94 V0
- Dow Tyril® 880B SAN
- 3M Safety-Walk™ 710 Black Coarse Tapes and Treads
- 3M 2A89 Co-Extruded Multi-Polymer Protect Tapes
Copyright © lookpolymers.com All Rights Reserved