Techmer ES HiFill® PA6 0180 B Barium Sulfate Filler
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6 0180 B Barium Sulfate Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Barium SulfateFeatures: High Specific GravityInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.6 MPa | 6900 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 50.3 MPa | 7300 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 167 °C | 333 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 - 1.00e+14 ohm-cm | 1.00e+13 - 1.00e+14 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Nyco NYGLOS® STPO Wollastonite
- Parker Chomerics CHO-BOND 1026 Conductive Silicone Splicing Compound
- DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66 (Unverified Data**)
- 3M Dyneon™ CCX1029 PTFE, 10% Carbon Fiber Filled (discontinued **)
- MarkeTech Repton 136 Aluminum Oxide
- Solvay RHODASURF® CET 2 Surfactant
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR Hi-Sil 233 Filler
- ExxonMobil Escorene™ FL 00623 Ethylene Vinyl Acetate Copolymer (European Grade)
- Perstorp Compounds Akestra™ 110 Thermoplastic Copolyester
- Braskem H 501HC Thermoforming Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved