- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Techmer ES HiFill® ABS GM30 LE 30% Glass Filled
Techmer ES HiFill® ABS GM30 LE 30% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® ABS GM30 LE 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightFeatures: Low ExtractablesInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Yield | 3.3 % | 3.3 % | ASTM D638 |
| Flexural Yield Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.00 J/cm @Thickness 3.17 mm |
7.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C | 16.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 218 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nilit Polynil® P50FL Externally Lubricated, Lightly Nucleated Nylon 66
- H.C. Starck Grade A Yttrium Oxide
- Techmer ES Elastoblend® PA6/6 GF13 IM2 HS L 13% Glass Filled
- Shin-Etsu Silicones LIMSâ„¢ KE2001-40A/B Elastomer
- Formosa Plastics Formolon® 165 PVC
- Eagle Brass 200/201 Nickel Alloy, Full Hardened
- Dow Corning FLUOROGEL® 4-8022
- Asahi Kasei Xyron® 740V Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved