SABIC Innovative Plastics LNP THERMOCOMP MF741XXH PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF741XXH PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MF741XXH is a compound based on Polypropylene reain containing Glass Fiber and proprietay antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added features include: high antimicrobial performance, high mechanical strength, healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.90 GPa | 711 ksi | 1 mm/min; ISO 527 |
| 5.30 GPa | 769 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 87.0 MPa | 12600 psi | ISO 178 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.40 GPa | 638 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
42.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 5 wt% Multi-Wall Carbon Nanotubes
- Quadrant EPP Ertalyte® PET-P, Polyester-semi-crystalline thermoplastic, extruded (ASTM Product Data Sheet)
- Parker Chomerics CHO-SEAL L6303 Conductive Elastomer
- PolyOne Geon™ Vinyl Dry Blend E7456 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Momentive Performance Materials IGS3713-D1 Insulating Glass Sealant, Black
- Shanghai Ofluorine D-1 PVDF Lithium Ion Battery Binders (DF-2)
- Zircar Ceramics IB-100B Alumina Bubble
- A. Schulman FORMION™ FI 301 Ionomer
- Beijing Evergrow Resources TBMH-30 Glass Fiber Tissue
- Plastics Group Polifil® RMT-20V 20% Talc-Reinforced Polypropylene, High Impact, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved