Techmer ES Elastoblend® PC IM
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified , Polycarbonate, Molded |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PC IM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Impact Modifier Features: Impact Modified Processing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Yield | 11 % | 11 % | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
4.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.14 J/cm @Thickness 6.35 mm, Temperature 22.8 °C |
4.00 ft-lb/in @Thickness 0.250 in, Temperature 73.0 °F |
ASTM D256 | |
| 8.54 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
16.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C | 38.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm | 380 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9840 TPE, ABS/PC Overmold
- NOVA Chemicals Novapol® LA-0218-AF LDPE Foam Resin (discontinued **)
- Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled
- Techmer ES Statiblend® PC FR BK
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- Tisan TISOPLEN® 30% Talc Filled Heat Stabilized Copolymer Polypropylene
- Eagle Brass 735 Nickel Silver 18%, Extra Hard
- Barlog Plastics KEBAFORM C 90 W POM Copolymer unreinforced, drinking water approved
- ACC Magnifoam™ MFSILTEC™-HD MTI Silicones Silicone Foam
- BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Dry)
Copyright © lookpolymers.com All Rights Reserved