Supreme Petrochem SP 6411 1924 Light Stabilized Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Supreme Petrochem SP 6411 1924 Light Stabilized Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics Prevents dust patterns due to static charges High gloss Good flow Improved light fastness Processing Injection molding Extrusion Applications A/C and cooler grill Material Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D792
Melt Flow	8.0 g/10 min @Load 5.00 kg, Temperature 200 Â°C	8.0 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	27.0 MPa	3920 psi	50 mm/min; ASTM D638
Elongation at Break	40 %	40 %	50 mm/min; ASTM D638
Flexural Strength	44.1 MPa @Thickness 3.20 mm	6400 psi @Thickness 0.126 in	ASTM D790
Flexural Modulus	2.06 GPa @Thickness 3.20 mm	299 ksi @Thickness 0.126 in	ASTM D790
Izod Impact, Notched	0.600 J/cm @Thickness 3.20 mm	1.12 ft-lb/in @Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	77.0 Â°C	171 Â°F	ASTM D648
Vicat Softening Point	96.0 Â°C	205 Â°F	1kg / 120Â°C; ASTM D1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+12 - 1.00e+13 ohm	1.00e+12 - 1.00e+13 ohm	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	<= 230 Â°C	<= 446 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F
Drying Temperature	60.0 - 80.0 Â°C	140 - 176 Â°F	( 2 hrs) Pre drying temp.