- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 66
- Nylon 66, 20% Glass Fiber Filled
- Techmer ES Elastoblend® PA6/6 GF15 IM HS L 15% Glass Filled
Techmer ES Elastoblend® PA6/6 GF15 IM HS L 15% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade , Nylon 66, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 GF15 IM HS L 15% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubricant and Impact ModifiedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 84.1 MPa | 12200 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.62 GPa | 525 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.92 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.60 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- NOVA Chemicals Gedexcel® 76L Expandable Polystyrene
- Micropol HD Polyethylene powders for cleaning products
- Karina 10/1075-IE White Color Concentrate MBU
- American Elements Holmium Nanoparticles
- American Elements Tantalum Nanoparticles
- DSM Akulon® F236-C Nylon 6 (European Grade) (Dry)
- EMS-Grivory Grivory® 1S XE 4224 nat PA1010
- Entec Hypel® PEHD20/.953 HDPE
- SABIC Innovative Plastics Lexan® HFD1731 PC Copolymer (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved