Supreme Petrochem SP 515 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 515 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Good flow properties Good balance of toughness and rigidity Available in any colorProcessing Injection molding Extrusion Applications Electrical switch boards MCB distribution boxes Electrical gang boxes Emergency light enclosures Enclosures of current transformer etc.Material Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.4 MPa | 4550 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa @Thickness 3.20 mm |
7690 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.57 GPa @Thickness 3.20 mm |
228 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 0.650 J/cm @Thickness 3.20 mm |
1.22 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 82.0 °C | 180 °F | IEC335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 95 % | 95 % | at 60°; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 93 |
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 250 °C | <= 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | ( 2 hrs) Pre drying temp. |
Users viewing this material also viewed the following:
- Nye Lubricants 774VHF-MS (NG) Synthetic Oil
- Network Polymers Softflex® 0350
- NOVA Chemicals Sclair® 19H Homopolymer HDPE Film Resin
- Polykemi AB SCANMID 6 B12^ QF2515 Nylon 6, Glass Fiber and Mineral Reinforced
- Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized
- DuPont Performance Polymers Delrin® SC655 NC010 Acetal Homopolymer (Unverified Data**)
- SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific)
- Solvay Specialty Polymers Tecnoflon® PL 557 Fluoroelastomer
- Wellman Wellamid® 22L-BL Engineering Grade Nylon 66
- DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR
Copyright © lookpolymers.com All Rights Reserved