Sumitomo Bakelite North America RX® 630 Fiberglass Reinforced Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 630 Fiberglass Reinforced Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RXÂ 630 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Information supplied by Sumitomo Bak North America.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | Powder; ISO 60 |
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Water Absorption | 0.050 % | 0.050 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | ISO 2039/2 |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ISO 527 |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| Flexural Modulus | 19.0 GPa | 2760 ksi | ISO 178 |
| Compressive Strength | 360 MPa | 52200 psi | ISO 604 |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature 23.0 °C |
7.78 µin/in-°F @Temperature 73.4 °F |
TMA |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | ASTM F433 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | As Molded; ISO 75 A |
| >= 282 °C | >= 540 °F | Post Baked; ISO 75 A | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 12.0 kV/mm @Thickness 3.00 mm |
305 kV/in @Thickness 0.118 in |
IEC 243 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Available Molding Grades | Compression, Transfer, Injection | |
| Color | Black, Green | |
| Form | Granular |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4003 RC 40% Glass Filled Polypropylene
- RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural
- NOVA Chemicals Novapol® LM-2522-A LDPE Injection Molding Resin
- Plenco 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **)
- Huntsman MY 720 Multifunctional Resin
- Multibase Dow Corning® MB50-0321 Siloxane Additive
- A. Schulman PP 1329 Polypropylene Stabilized Copolymer Polypropylene
- Dow Corning SE 4446 CV KIT
- Ashley Polymers Ashlene® LT940H Nylon 11
Copyright © lookpolymers.com All Rights Reserved