Hexcel® HexPly® F155 Epoxy Resin, W3T282 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F155 Epoxy Resin, W3T282 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: W3T282-42"-F155; Fiber: T300 Toho®Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 6.481 MPa @Temperature 24.0 °C |
940.0 psi @Temperature 75.2 °F |
Flatwise TS |
| 848 MPa @Temperature 24.0 °C |
123000 psi @Temperature 75.2 °F |
||
| Tensile Modulus | 58.0 GPa @Temperature 24.0 °C |
8410 ksi @Temperature 75.2 °F |
|
| Compressive Yield Strength | 496 MPa @Temperature 71.0 °C |
71900 psi @Temperature 160 °F |
|
| 904 MPa @Temperature 24.0 °C |
131000 psi @Temperature 75.2 °F |
||
| Compressive Modulus | 57.2 GPa @Temperature 24.0 °C |
8300 ksi @Temperature 75.2 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.022 | Laminate |
| Dry Resin Content (%) | 40-44 | Prepreg |
| Fiber Volume (%) | 50 | Laminate |
| Flow (%) | 4-16 |
Users viewing this material also viewed the following:
- Hong Kun Group HATU Pharmaceutical Intermediate
- Indium Corp. Indalloy® 263 Tin-Silver-Copper Solder Alloy
- Henkel Hysol EA 9380.05 Paste Adhesive System
- Sylvin Technologies 9999-80 Natural PVC Molding Compound
- Sibur 1045-12 Compound 948 Polyvinyl Chloride (PVC)
- A. Schulman PP 1102-01 Polypropylene General Purpose, Molding Grade Polypropylene
- Washington Penn Homopolymer Polypropylene 40% Talc Filled
Copyright © lookpolymers.com All Rights Reserved