Sumitomo Bakelite North America RXÂ® 3-2-520F-P Short-Glass Reinforced Diallyl Phthalate

Category	Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America RXÂ® 3-2-520F-P Short-Glass Reinforced Diallyl Phthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SIG-FInformation provided by Sumitomo Bak North America, Inc.

Physical Properties	Metric	English	Comments
Density	1.90 g/cc	0.0686 lb/inÂ³	ASTM D792
Apparent Bulk Density	0.790 g/cc	0.0285 lb/inÂ³
Water Absorption	0.25 %	0.25 %	48 hours, 50Â°C. ASTM D570
Linear Mold Shrinkage	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	Compression Molding. ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	83.0 MPa	12000 psi	ASTM D638
Flexural Yield Strength	131 MPa	19000 psi	ASTM D790
Flexural Modulus	12.4 GPa	1800 ksi	ASTM D790
Compressive Yield Strength	152 MPa	22000 psi	ASTM D695
Izod Impact, Notched	0.430 J/cm	0.806 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	18.0 Âµm/m-Â°C @Temperature 20.0 Â°C	10.0 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM D696
Maximum Service Temperature, Air	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	274 Â°C	525 Â°F	ASTM D648A
UL RTI, Electrical	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical with Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical without Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	39 %	39 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.9 @Frequency 1e+6 Hz	3.9 @Frequency 1e+6 Hz	Wet
	4.1 @Frequency 1000 Hz	4.1 @Frequency 1000 Hz	Wet
Dielectric Strength	16.0 kV/mm	406 kV/in	Wet, step-by-step. ASTM D149
	18.0 kV/mm	457 kV/in	Wet, short term. ASTM D149
Dissipation Factor	0.010 @Frequency 1000 Hz	0.010 @Frequency 1000 Hz	Wet; ASTM D150
	0.013 @Frequency 1e+6 Hz	0.013 @Frequency 1e+6 Hz	Wet; ASTM D150
Arc Resistance	150 sec	150 sec	ASTM D495
Comparative Tracking Index	>= 600 V	>= 600 V	UL746A, ASTM D3638
Hot Wire Ignition, HWI	>= 120 sec @Thickness 1.70 mm	>= 120 sec @Thickness 0.0669 in	UL PLC 0 (120+ sec)
High Amp Arc Ignition, HAI	120 arcs @Thickness 1.70 mm	120 arcs @Thickness 0.0669 in
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 1.70 mm	0.000 - 0.394 in/min @Thickness 0.0669 in	UL PLC 0 (0-10 mm/min)

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 180 Â°C	320 - 356 Â°F	Mold temperature