Carmel Olefins CAPILENE® E 65 F Polypropylene Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Carmel Olefins
Trade Name	CAPILENE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carmel Olefins CAPILENE® E 65 F Polypropylene Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: CAPILENE® E 65 F is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). It exhibits good processability, easy film stretchability and good mechanical properties.Applications: Typical applications for CAPILENE® E 65 F are BOPP plain or coextruded packaging films. It doesn't contain slip or antiblock additives and is also calcium stearate free, therefore it is suitable for production of metallizable BOPP film.CAPILENE® E 65 F is also used with the extrusion and coextrusion thermoforming process were melt strength is of importance.Information provided by Carmel Olefins.

Physical Properties	Metric	English	Comments
Melt Flow	1.9 g/10 min @Load 2.16 kg, Temperature 230 °C	1.9 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	33.0 MPa	4790 psi	50 mm/min; ASTM D638
Elongation at Yield	15 %	15 %	50 mm/min; ASTM D638
Flexural Modulus	1.50 GPa	218 ksi	ASTM D790
Izod Impact, Notched	0.400 J/cm	0.749 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	94.0 °C	201 °F	ASTM D648
Vicat Softening Point	155 °C @Load 1.02 kg	311 °F @Load 2.25 lb	ASTM D1525