Sumitomo Bakelite North America FM 4005X4649 Fiberglass Reinforced Phenolic Novolac

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America FM 4005X4649 Fiberglass Reinforced Phenolic Novolac.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FM 4005X4649 a fiberglass reinforced two-step phenolic molding compound formulated to increase thermal conductivity, to provide static dissipation and good wear resistance to abrasive media.Information supplied by Sumitomo Bak North America.

Physical Properties	Metric	English	Comments
Bulk Density	0.750 g/cc	0.0271 lb/in³	Powder; ASTM D1895
Density	1.83 g/cc	0.0661 lb/in³	ASTM D-792
Water Absorption	0.070 %	0.070 %	24 hour; ASTM D570
	0.20 %	0.20 %	48 hour; ASTM D570
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	90	90	ASTM D785
Tensile Strength, Ultimate	48.0 MPa	6960 psi	ASTM D638
Flexural Strength	105 MPa	15200 psi	ASTM D790
Flexural Modulus	14.0 GPa	2030 ksi	ASTM D790
Compressive Strength	210 MPa	30500 psi	ASTM D695
Izod Impact, Notched	0.220 J/cm	0.412 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	29.0 µm/m-°C @Temperature 20.0 °C	16.1 µin/in-°F @Temperature 68.0 °F	ASTM E831
Thermal Conductivity	0.750 W/m-K	5.20 BTU-in/hr-ft²-°F	ASTM C518
Maximum Service Temperature, Air	150 °C	302 °F	UL Temperature Index; UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	195 °C	383 °F	As Molded; ASTM D648A
	>= 282 °C	>= 540 °F	Post Baked; ASTM D648A
Flammability, UL94	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Descriptive Properties	Value	Comments
Available Molding Grades	Compression, Transfer, Injection
Color	Black
Form	Granular