Sumitomo Bakelite North America 52-20-30 Short-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America 52-20-30 Short-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.290 g/cc | 0.0105 lb/in³ | |
| Water Absorption | 0.35 % | 0.35 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0035 cm/cm | 0.0015 - 0.0035 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Flexural Yield Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Compressive Yield Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 20.0 °C |
11.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.306 W/m-K | 2.12 BTU-in/hr-ft²-°F | ASTM F433 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648A |
| Oxygen Index | 21 % | 21 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.2 @Frequency 1e+6 Hz |
4.2 @Frequency 1e+6 Hz |
Wet |
| 4.4 @Frequency 1000 Hz |
4.4 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, step-by-step. ASTM D149 |
| 15.0 kV/mm | 381 kV/in | Wet, short term. ASTM D149 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Wet; ASTM D150 |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
Wet; ASTM D150 | |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL746A, ASTM D3638 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Users viewing this material also viewed the following:
- Hong Kun Group HBTU Pharmaceutical Intermediate
- Kingfa PBT-RG302 Flame Retardant, 30% Glass Fiber Reinforced PBT
- Indium Corp. Indalloy® 256 96.5Sn/3.0Ag/0.5Cu Lead-Free Solder Alloy
- Taiwan PU Corporation TPU-BH95 Hydrolysis Resistance, Blow Molding Polyether Base TPU
- Shamrock Technologies Fluoro T® 715 Thermoplastic Grade PTFE Additive
- SolVin 386NB Polyvinyl Chloride Low Viscosity Paste
- Lubrizol Pellethane® 2363-65D Thermoplastic Polyurethane Elastomer
- Lanxess Pocan® DP B 3235 XF 901510 PBT, 30% Glass Fiber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved