Loxim 140 01V0 Polycarbonate, 40% Glass Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 140 01V0 Polycarbonate, 40% Glass Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 - 130 MPa | 17400 - 18900 psi | ASTM D683 |
| Elongation at Break | >= 2.0 % | >= 2.0 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 - 1.20 J/cm | 1.87 - 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 - 155 °C | 302 - 311 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PA1503 Polyamide 6 with - Carbon Nanotube Masterbatch
- SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Europe-Africa-Middle East)
- Dielectric Polymers NT-711 Electrical/Mechanical Tape (discontinued **)
- Quadrant EPP Duratron® PBI CU60 Polybenzimidazole, unfilled, compression molded (ASTM Product Data Sheet)
- MarkeTech W90Cu Tungsten/Copper Heat Sink Material
- Sumitomo Bakelite Durez® 23570 Phenolic, Injection Grade
- A. Schulman PP 984 Polypropylene Medium Impact Polypropylene
- Borealis LE0310-44 Polyethylene Compound, Crosslinkable, Semiconductive
- Advanced Polymer Alloys Alcryn® 2250 UT Melt Processable Rubber
- LATI LARAMID CE/60 60% Mineral Filled Polyphthalamide (PPA) Based Compound (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved