Styron MAGNUMâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron MAGNUMâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: MAGNUMâ„¢ 3904 is a resin with super-high impact. It is used in a wide range of technical applications. It can be processed by injection molding, extrusion or thermoforming. The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-coloring.Applications: TransportationProtective coversLeisureAutomotive interior trimLuggageInformation provided by Styron
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183/B
Apparent Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ISO 294-4
Melt Flow 4.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 60
Mechanical Properties Metric English Comments
Tensile Strength, Yield 37.0 MPa

@Thickness 3.20 mm
 5370 psi

@Thickness 0.126 in
 Injection Molded; ISO 527-2/50
39.0 MPa

@Thickness 3.20 mm
 5660 psi

@Thickness 0.126 in
 Injection Molded; ISO 527-2/100
Elongation at Yield 2.6 %

@Thickness 3.20 mm
 2.6 %

@Thickness 0.126 in
 Injection Molded; ISO 527-2/50
2.8 %

@Thickness 3.20 mm
 2.8 %

@Thickness 0.126 in
 Injection Molded; ISO 527-2/100
Tensile Modulus 1.82 GPa

@Thickness 3.20 mm
 264 ksi

@Thickness 0.126 in
 Injection Molded; ISO 527-2
Flexural Strength 58.0 MPa

@Thickness 3.20 mm
 8410 psi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Flexural Modulus 1.90 GPa

@Thickness 3.20 mm
 276 ksi

@Thickness 0.126 in
 3-points, 2 mm/min, Injection Molded; ISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 180/A
42.0 kJ/m²

@Temperature 23.0 °C
 20.0 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 180/A
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/2
1.80 J/cm²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/1eA
2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/2
3.70 J/cm²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
Annealed; ISO 75-2/A
Vicat Softening Point 97.0 °C
207 °F
ISO 306/B50
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Flame Spread 40.0 mm/min
1.57 in/min
ISO 3795
Descriptive Properties Value Comments
Carbon Emission 200 µg/g
VDA 277