Styron EMERGEâ„¢ 8702 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 8702 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 8702 advanced resin is an ignition-resistant, 20% glass reinforced, polycarbonate resin. This resin contains no bromide, chloride, or phosphate additives. It is a medium flow PC resin with a mold release system, intended for injection molding applications. Applications: Information Technology Equipment Electrical Parts Other structural/internal parts Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ASTM D638 |
| Flexural Strength | 170.0 MPa | 24650 psi | ASTM D790 |
| Flexural Modulus | 5.499 GPa | 797.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.2 µm/m-°C @Temperature -40.0 - 82.2 °C |
14.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 52.2 µm/m-°C @Temperature -40.0 - 82.2 °C |
29.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | >= 135 °C | >= 275 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | unannealed; ASTM D648 |
| 143 °C | 289 °F | annealed; ASTM D648 | |
| Vicat Softening Point | 150 °C | 302 °F | 50°C/hr, 50N; ASTM D1525 |
| 160 °C | 320 °F | 120°C/hr, 10N; ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Oxygen Index | 35 % | 35 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 1.00 - 3.00 mm |
1760 °F @Thickness 0.0394 - 0.118 in |
IEC 60695-2-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm @Thickness 1.80 mm |
1.00e+16 ohm-cm @Thickness 0.0709 in |
ASTM D257 |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.1 @Thickness 1.60 mm, Frequency 10.0 - 1.00e+6 Hz |
3.1 @Thickness 0.0630 in, Frequency 10.0 - 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | >= 27.2 kV/mm @Thickness 1.60 mm |
>= 692 kV/in @Thickness 0.0630 in |
ASTM D149 |
| Dissipation Factor | 0.0025 @Frequency 100 Hz |
0.0025 @Frequency 100 Hz |
ASTM D150 |
| 0.0050 @Frequency 10 Hz |
0.0050 @Frequency 10 Hz |
ASTM D150 | |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 175 V @Thickness 3.00 mm |
175 V @Thickness 0.118 in |
IEC 60112 |
Users viewing this material also viewed the following:
- Polykemi AB POLYlux 3709M PC/PBT-Blend
- NOVA Chemicals Novapol® TR-0735-U Hexene MDPE Rotational Molding Resin
- Nilit FRIANYL A63 V0 G5 Nylon 6.6 for injection molding, 25% glass fiber reinforced
- SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N774 (SRF) Filler
- Teknor Apex Telcar® TL EF-6100 Thermoplastic Elastomer
- Unipetrol Light Stabilized Oil Hydrogenate
- Eagle Brass 725 Copper Nickel Tin, Hard
- Sumitomo Bakelite North America RX® 655 Novolac Phenolic
- BASF Ultradur® B 4300 G3 High Speed 15% Glass Filled BK 15045 PBT
Copyright © lookpolymers.com All Rights Reserved