- Styron CALIBREâ„¢ 2061-6 Polycarbonate
Styron CALIBREâ„¢ 2061-6 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 2061-6 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CALIBREâ„¢ 2061-6 resin is used in applications involving steam or ethylene oxide for sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 23°C, 24hrs; ASTM D570 |
| Water Absorption at Saturation | 0.32 % | 0.32 % | 23°C, 50% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | 3-points, 2 mm/min; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 3-points, 2 mm/min; ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm | 17.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Tensile Impact | 149 J/cm | 280 ft-lb/in | ASTM D1822 |
| Dart Drop, Total Energy | 90.0 J | 66.4 ft-lb | 8000 ipm; ASTM D3763 |
| Abrasion | 45 | 45 | [%] Taber Abrasion Resistance - Δ; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.4 µm/m-°C @Temperature -40.0 - 82.2 °C |
38.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | unannealed; ASTM D648 |
| 142 °C | 288 °F | annealed; ASTM D648 | |
| Vicat Softening Point | 157 °C | 314 °F | 50°C/hr, 50N; ASTM D1525 |
| Flammability Test | 1.0 | 1.0 | [in] Average Extent of Burning; ASTM D635 |
| Oxygen Index | 26 % | 26 % | ISO 4589-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60 Hz |
3.0 @Frequency 60 Hz |
ASTM D150 |
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-113 LDPE General Purpose Packaging Resin (discontinued **)
- Solvay Specialty Polymers Algoflon® L203 Polytetrafluoroethylene (PTFE) (Unverified Data**)
- Teknor Apex APEX® 84842-B Polyvinyl Chloride, Flexible
- Wico Plast Wicoran 47 ABS, Impact Resistant
- Zircar Refractory Composites RS-99-45 Refractory Sheet
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR Hi-Sil 233 Filler
- Alliance Polymers Viprene™ G80A-32U-NAT Thermoplastic Vulcanizate Elastomer
- PolyOne Synprene® RT-5155 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved