Styrolution Zylar 650 MBS
| Category | Polymer , Thermoplastic , Acrylic (PMMA) |
| Manufacturer | Styrolution |
| Trade Name | Zylar |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Zylar 650 MBS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zylar® 650 is an impact modified styrene acrylic copolymer that provides a balance of clarity and toughness, with outstanding strength and rigidity. Zylar 650 also has superior processing characteristics for demanding injection molded applications.Good balance of toughness, stiffness, and clarityLow densityEase of processingGamma & ETO sterilizableMeets USP XXIII specifications for Class VI plasticsInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D 792 |
| Water Absorption at Saturation | 0.10 % @Temperature 23.0 °C |
0.10 % @Temperature 73.4 °F |
ASTM D 570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D 955 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D 785 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D 638 |
| Elongation at Break | 40 % | 40 % | ASTM D 638 |
| Tensile Modulus | 2.14 GPa | 310 ksi | ASTM D 638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D 790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D 256 |
| Gardner Impact | 16.9 J | 12.5 ft-lb | ASTM D 5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 249 °C | 480 °F | |
| Vicat Softening Point | 98.9 °C @Load 1.02 kg |
210 °F @Load 2.25 lb |
120°C/h; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.57 | 1.57 | Sodium D Line; ASTM D 542 |
| Haze | 2.0 % | 2.0 % | ASTM D 1003 |
| Transmission, Visible | >= 90 % @Wavelength 550 nm |
>= 90 % @Wavelength 550 nm |
ASTM D 1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 238 °C | 400 - 460 °F | |
| Mold Temperature | 26.7 - 54.4 °C | 80.0 - 130 °F | |
| Drying Temperature | 65.6 °C @Time 7200 sec |
150 °F @Time 2.00 hour |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E50E Ethylene Propylene Rubber
- Karina 810-37/3-CRB Ocher PVC Compound
- SABIC Innovative Plastics NORYL WCD825 PPE-TPE (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp DF0066P PC
- Wico Plast Wicotal 90 Acetal
- Zircar Refractory Composites RS-A Refractory Sheet
- A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene
- EMS-Grivory Grivory® XE 4105 black 9992 PA610-GF50
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Non-Black Sulfur Cure
- Lehmann & Voss LUVOCOM® 1105-8339 PEEK, lubricant modified
Copyright © lookpolymers.com All Rights Reserved