Styrolution Terluran® HD-15 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® HD-15 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 15.75 g/10 min @Load 10.0 kg, Temperature 220 °C |
15.75 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | Nominal; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 17.0 J/cm² @Temperature 23.0 °C |
80.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C | 52.8 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75 |
| Vicat Softening Point | 100 °C @Temperature 50.0 °C |
212 °F @Temperature 122 °F |
ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm @Thickness 1.50 mm |
940 kV/in @Thickness 0.0591 in |
K20/P50; IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | North America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer
- Mearthane Durethaneâ„¢ S DS-685A Solid Polyurethane Elastomer
- Lucobit Lucofin® 1412-t3 Polyolefin TPO Granules, Light Grey
- LATI Latamid 66 PA 66
- Techmer ES Luriblend® PA6/6 GF43 ML2 43% Glass Filled
- Styron CALIBREâ„¢ 301V-6 Polycarbonate Resin
- A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene
- Adell AR-33 Nylon 66, 15% Glass Reinforced
- Carpenter Four Star High Speed Steel Red-Wear® (AISI M4)
- Overview of materials for Ethylene Butyl Acrylate
Copyright © lookpolymers.com All Rights Reserved