Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Conditioned)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon
Manufacturer Styrolution
Trade Name Terblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Terblend N NG-02 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, high impact strength and good surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
dry; ISO 1183
Moisture Absorption at Equilibrium 1.3 %
1.3 %
beginning dry (23°C/50% R.H.); ISO 62
Melt Flow 14 g/10 min

@Load 10.0 kg,
Temperature 240 °C
14 g/10 min

@Load 22.0 lb,
Temperature 464 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 48.0 MPa
6960 psi
5mm/min; ISO 527
Tensile Strength, Yield 39.0 MPa
5660 psi
2 in/min; ASTM Test
Elongation at Break 4.0 %
4.0 %
5mm/min; ISO 527
8.0 %
8.0 %
0.2 in/min; ASTM Test
Tensile Modulus 2.21 GPa
321 ksi
ASTM Test
2.40 GPa
348 ksi
1mm/min; ISO 527
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+11 ohm-cm
>= 1.00e+11 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 60093
Dielectric Constant 3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 36.0 kV/mm
914 kV/in
IEC 60243-1
Dissipation Factor 0.050

@Frequency 1.00e+6 Hz
0.050

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 550 V
550 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 265 °C
509 °F
Injection molding
Injection Velocity 65.0 mm/sec
2.56 in/sec
Injection molding
Descriptive Properties Value Comments
Commercial Status Active America
Primary Processing Technique Injection Molding
UL.UL-C Yes