Styrolution PS 2710 HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Styrolution PS 2710 HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 2710 is a high impact grade of polystyrene with improved stress crack resistance, developed for extrusion and thermoforming applications, especially for the refrigerator industry.Improved Environmental stress cracking resistance (ESCR) HIPSBalanced mechanical propertiesInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % <br>@Temperature 23.0 °C |
<= 0.10 % <br>@Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % <br>@Temperature 23.0 °C |
<= 0.10 % <br>@Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 5.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 °C |
5.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 65.0 MPa | 9430 psi | ISO 2039-1 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Elongation at Yield | 1.8 % | 1.8 % | ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527 |
| Flexural Strength | 32.0 MPa | 4640 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² <br>@Temperature -30.0 °C |
3.33 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 180/A |
| 12.0 kJ/m² <br>@Temperature 23.0 °C |
5.71 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 10.2 J/cm² <br>@Temperature -30.0 °C |
48.5 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 179 |
| NB <br>@Temperature 23.0 °C |
NB <br>@Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² <br>@Temperature -30.0 °C |
3.33 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 179 |
| 1.00 J/cm² <br>@Temperature 23.0 °C |
4.76 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ISO 75 |
| Vicat Softening Point | 92.0 °C <br>@Load 5.10 kg |
198 °F <br>@Load 11.2 lb |
50°C/h; ISO 306 |
| 97.0 °C <br>@Load 1.02 kg |
207 °F <br>@Load 2.25 lb |
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 20 % | 20 % | Specular Gloss, 60°; ASTM D 523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.5 <br>@Frequency 100 Hz |
2.5 <br>@Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 155 kV/mm <br>@Thickness 1.50 mm |
3940 kV/in <br>@Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.00040 <br>@Frequency 100 Hz |
0.00040 <br>@Frequency 100 Hz |
IEC 60250 |
| 0.00040 <br>@Frequency 1.00e+6 Hz |
0.00040 <br>@Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5020 PD1 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- PolyMirae Moplen EP500N Injection Molding Grade Polypropylene
- A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene
- Dow Corning HV 495 Emulsion
- Azoty Tarnow™ Tarnamid® T-27 GF10 MX6 Polyamide 6 - Flame Retarded, Reinforced
- ATI Allvac® Nickelvac® 304 L UNS S30403 Specialty Steel
- 3M 519YP2 Sandblast Stencil
- SABIC Innovative Plastics LNP STAT-KON ME006 PP (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved