Star Plastics PC/ABSQX7002 Molding Grade PC/ABS High Flow

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Star Plastics, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics PC/ABSQX7002 Molding Grade PC/ABS High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.1 MPa
9000 psi
ASTM D638
Tensile Modulus 2.34 GPa
340 ksi
ASTM D638
Flexural Yield Strength 96.5 MPa
14000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 5.87 J/cm
11.0 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
unannealed, .125in; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 274 °C
450 - 525 °F
Middle Barrel Temperature 246 - 288 °C
475 - 550 °F
Front Barrel Temperature 246 - 288 °C
475 - 550 °F
Nozzle Temperature 246 - 288 °C
475 - 550 °F
Melt Temperature 246 - 288 °C
475 - 550 °F
Mold Temperature 57.2 - 85.0 °C
135 - 185 °F
Drying Temperature 82.2 - 110 °C
180 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour
Back Pressure 0.138 - 0.689 MPa
20.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm