Skamol Group SUPER 1100 E Calcium Silicate Insulating Slab

Category	Ceramic , Oxide , Silicon Oxide
Manufacturer	Skamol Group
Trade Name	Super
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Skamol Group SUPER 1100 E Calcium Silicate Insulating Slab.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

SKAMOL SUPER calcium silicate slabs have the following characteristics: Max. service temperature: Up to 1100Â°C (2012Â°F)Back-up insulation onlyExtremely lightweightVery low thermal conductivityExcellent mechanical strengthCan be used in furnaces with reducing atmosphere due to their high resistance to carbon monoxide and hydrocarbonsDesigned for the application as back-up insulation of all refractory constructionsThe ideal choice for efficient insulation of kilns, furnaces, ovens, stoves, boilers, soaking pits, regenerators, mains and other combustion equipmentThe combination of low weight, high service temperature and good integrity makes the calcium silicate slabs highly applicable as fire protection in several applications.Information provided by Skamol.

Physical Properties	Metric	English	Comments
Bulk Density	0.245 g/cc	0.00885 lb/inÂ³	Dry
Loss On Ignition	6.00 % @Temperature 1025 Â°C	6.00 % @Temperature 1877 Â°F
Porosity	90 %	90 %	Total
Permeability	0.50	0.50	nPm, Permeability to Air; BS EN 993-4: 1995

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00180 GPa	0.261 ksi	EN 993-6: 1995
Compressive Strength	2.70 MPa	392 psi	EN 1094-5: 1995

Thermal Properties	Metric	English	Comments
CTE, linear	5.50 Âµm/m-Â°C @Temperature 20.0 - 750 Â°C	3.06 Âµin/in-Â°F @Temperature 68.0 - 1380 Â°F	BSÂ 1902: section 5.3: 1990
Specific Heat Capacity	0.840 J/g-Â°C	0.201 BTU/lb-Â°F
Thermal Conductivity	0.0700 W/m-K @Temperature 200 Â°C	0.486 BTU-in/hr-ftÂ²-Â°F @Temperature 392 Â°F	Mean temp.; ASTMÂ C-182
	0.0900 W/m-K @Temperature 400 Â°C	0.625 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F	ASTMÂ C-182
	0.100 W/m-K @Temperature 600 Â°C	0.694 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F	ASTMÂ C-182
Maximum Service Temperature, Air	1100 Â°C	2010 Â°F
Shrinkage	1.50 % @Time 43200 sec	1.50 % @Time 12.0 hour	Linear Reheat Shrinkage, 12h at 50Â°C (122Â°F) below max. service temp.; EN 1094-6: 1999

Component Elements Properties	Metric	English
Al2O3	0.30 %	0.30 %
CaO	45 %	45 %
Fe2O3	0.30 %	0.30 %
K2O	0.10 %	0.10 %
MgO	0.60 %	0.60 %
Na2O	0.10 %	0.10 %
SiO2	47 %	47 %

Descriptive Properties	Value	Comments
Color	Grey
Creep in Compression	0.4 %	BS EN 993-9: 1997, 50h at 900Â°C (1652Â°F), load 0.1 MPa (14.5 psi)
Pyrometric Cone Equivalent	1345Â°C	ASTM C24-89, ORTON cones