Star Plastics PC721HFR Molding Grade PC High Flow with Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PC721HFR Molding Grade PC High Flow with Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Tensile Modulus | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Yield Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.38 GPa | 345 ksi | ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm | 13.0 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | .062in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 246 - 274 °C | 475 - 525 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 274 - 302 °C | 525 - 575 °F | |
| Nozzle Temperature | 274 - 302 °C | 525 - 575 °F | |
| Melt Temperature | 274 - 302 °C | 525 - 575 °F | |
| Mold Temperature | 71.1 - 98.9 °C | 160 - 210 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJAF111L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polykemi AB POLYfill PPH GF5020 PD1 VT2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled, Heat Stabilized
- SABIC Innovative Plastics ULTEM 2200F PEI (Europe-Africa-Middle East)
- Techmer ES HiFill FR® PA6/6 GF25 FR BK 25% Glass Filled (Conditioned)
- Stellarchem GP-975 TPE Compound
- Goodfellow Nickel 55/Titanium 45 Shape Memory Alloy
- ACC QLE 1050 QSI Quantum Silicones 30 Durometer Clear, Addition Cure, 1-part Elastomer for Coating
- Braskem IA59 HDPE Injection Molding Polyethylene Homopolymer
- DuPont Bynel® 20E482 Acid-Modified Ethylene Terpolymer Adhesive Resin (discontinued **)
- A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved